| Polymer Properties |
|
|
|
| Density |
863 |
kg/m³ |
ASTM D792 |
| Melt Flow Rate (MFR) |
|
|
|
| At 190°C and 2.16 kg |
13.0 |
g/10 min |
ASTM D1238 |
| At 230°C and 2.16 kg |
27.0 |
g/10 min |
ASTM D1238 |
| Mooney Viscosity |
|
|
|
| ML1+4, 121°C |
3 |
MU |
ASTM D1646 |
| Mechanical Properties |
|
|
|
| Tensile Properties |
|
|
|
| Tensile Strength at Break |
2.3 |
MPa |
ASTM D638 |
| Elongation at Break |
> 1000 |
% |
ASTM D638 |
| 100% Modulus |
1.8 |
MPa |
ASTM D638 |
| Durometer Hardness |
|
|
|
| Shore A (1 sec) |
63 |
– |
ASTM D2240 |
| Shore D (1 sec) |
13 |
– |
ASTM D2240 |
| Flexural Modulus (1% Strain) |
7.5 |
MPa |
ASTM D790 |
| Tear Strength (Type C) |
25.5 |
kN/m |
ASTM D624 |
| Thermal Properties |
|
|
|
| Peak Melting Temperature |
42 |
°C |
Sabic Industrial Method |
| Glass Transition Temperature, Tg |
-56 |
°C |
Sabic Industrial Method |